Dacromet processing folder doll treatment, noting that what matters? : 1. DACROMET case of light will deteriorate rapidly, so the coating process should DACROMET indoors. 2. DACROMET baking temperature is too low, too high will cause the loss of corrosion resistance DACROMET, DACROMET should be baked in a suitable temperature range. 3. DACROMET life cycle is very short, so it should run out as soon as possible. 4. DACROMET poor wear resistance, it should DACROMET primer, then cover with other coating wear closed. Process about the process: organic solvent degreasing - mechanical blasting - Spraying - Baking - secondary painting - baking - dry. Little lies: 1. High heat resistance: Dacromet high temperature corrosion can heat up to temperatures above 300 ℃. The traditional galvanizing process, when the temperature reaches 100 ℃ had been scrapped from the skin. 2. The superior corrosion resistance: Dacromet film thickness is only 4-8μm, but the rust is 7-10 times more than conventional electro-galvanized, hot dip galvanized or paint coating method. Standard parts are DACROMET Process and fittings through more resistant to salt spray test 1200h red rust did not appear. 3. Good permeability: due to electrostatic shielding effect, the workpiece deep slit, fittings and other parts of the inner wall of the zinc plating is difficult, so the above parts of the workpiece can not be protected by plating method. DACROMET you can enter these parts of the workpiece to form Dacromet. 4. No hydrogen embrittlement: Dacromet treatment process determines DACROMET no hydrogen embrittlement, it is ideal for coating DACROMET force member. 5. Good adhesion and recoat properties: Dacromet and base metal have good adhesion, and strong adhesion with other additional coatings, spraying the parts treated easily colored, in combination with organic coating force even more than the phosphate coating. Dacromet processing, environmental protection Dacromet processing, black Dacromet processing www.czrhdkl.top